201 plaques en acier inoxydable N° 1 finition HR
Notre contact
TIANJIN TEDA GANGHUA TRADE CO.,LTD
Sandy Wei / Directeur des ventes
NORME : AISI, ASTM, GB, EN, DIN, JIS, etc
Nom du moulin : TISCO, Baosteel, LISCO, ZPCC, JISCO, EST etc
Grade : 201 202 301 302 303 304 304L 309S 310S 316 316L 316Ti 321 409L 410 410S 420 420JS 429 430 436L 439 441 443 444 445 446 904L 2205 2507, 0Cr13, 1Cr13, 2Cr13, 3Cr13, 3Cr12, DIN 1.4021, 1.4028, 1.4016, 1.4521, 1.4113, 1.4003, 1.4512, 1.4845, 1.4833, 1.4541, 1.4404, 1.4301, 1.4307, 1.4318, 1.4006
Dimensions : épaisseur 0.02 ~ 200 mm ; largeur : 8 ~ 1800 mm ; longueur : selon les exigences du client. Largeur standard*longueur: 1000*2000mm, 1000*30000mm, 1219*2438mm; 4 pieds*8 pieds, 1500*3000mm, 1500*6000mm etc
Finition : N° 1, 2D, 2B, BA, 8K, Miroir, SB, Hairline, HL, N° 3, 4, Décapage, Embossé, Type doré-Ti enduit, Teardrop etc.
Commande minimum: 1 feuille
Emballage : emballage standard à exporter, veuillez consulter les photos d'emballage suivantes pour référence :
1) repasser les palettes avec du papier étanche et une bande d'acier.
2) palettes en bois avec papier étanche et bande d'acier.
Poids de chaque emballage max. 4.0 tonne
Conditions de paiement :
1) 30% T/T comme dépôt, le solde est contre B/L copie.
2) L/C irrévocable en vue ouvert par First-Class Bank.
3) selon les exigences détaillées du client
1) stock en entrepôt pour taille et grade réguliers 2) selon la quantité du client. En général, nous pouvons expédier les marchandises dans les 3 jours après avoir obtenu votre commande ferme.
Utilisation finale : l'acier est particulièrement adapté à une utilisation architecturale, aux pièces de brûleur à combustible, aux appareils ménagers, aux pièces d'appareils ménagers. Tours automatiques, boulons et écrous, réservoirs d'eau chaude, systèmes d'eau chaude, appareils sanitaires, appareils ménagers durables, volant de bicyclettes, etc
Si vous êtes intéressé par ce programme, veuillez vous adresser à Faites-le moi savoir.
Je vais vous répondre Dès que possible.
Cordialement,
Wei sablonneux
Nom standard |
Composition chimique |
Propriétés mécaniques |
JIS |
GO |
AIST |
FR |
C |
Si |
Mn |
P |
S |
Ni |
CR |
Autres |
Limite d'élasticité |
Traction |
Allongement |
Dureté |
S/N |
max |
max |
max |
max |
max |
max |
N/mm2 |
N/mm2 |
% |
HAUTE TENSION |
HRB |
Aciers inoxydables austénitiques |
SUS201 |
1Cr17Mn6Ni5N |
201 |
** |
0.15 |
1 |
5.50-7.50 |
0.06 |
0.03 |
1 |
16.00-18.00 |
N0.25 |
245 |
640 |
40 |
253 |
100 |
SUS202 |
1Cr18Mn8Ni5N |
202 |
** |
0.15 |
1 |
7.50-10.00 |
0.06 |
0.03 |
4.00-6.00 |
17.00-19.00 |
N0.25 |
245 |
590 |
40 |
218 |
95 |
SUS301 |
1Cr17Ni7 |
301 |
1.431 |
0.15 |
1 |
2 |
0.045 |
0.03 |
6.00-8.00 |
16.00-18.00 |
_ |
≥ 205 |
≥ 520 |
≥ 40 |
≤218 |
≤95 |
SUS301L |
00Cr17Ni7 |
301L |
1.4318 |
0.03 |
1 |
2 |
0.045 |
0.03 |
6.00-8.00 |
16.00-18.00 |
N0.20 |
≥ 215 |
≥ 550 |
≥ 45 |
≤218 |
≤95 |
SUS304 |
0Cr18Ni9 |
304 |
1.4301 |
0.08 |
1 |
2 |
0.045 |
0.03 |
8.0-10.50 |
18.00-20.00 |
_ |
≥ 205 |
≥ 520 |
≥ 40 |
≤200 |
≤90 |
SUS304L |
00Cr19Ni10 |
304L |
1.4307 |
0.03 |
1 |
2 |
0.045 |
0.03 |
9.00-13.00 |
18.00-20.00 |
_ |
≥ 175 |
≥ 480 |
≥ 40 |
≤200 |
≤90 |
SUS304CU |
0Cr18Ni9 |
304 |
1.4301 |
0.08 |
1 |
2 |
0.045 |
0.03 |
8.00-10.50 |
18.00-20.00 |
Cu 0.70-1.30 |
≥ 205 |
≥ 520 |
≥ 40 |
≤200 |
≤90 |
SUS304Ni8.5 |
0Cr18Ni9 |
304 |
1.4301 |
0.08 |
1 |
2 |
0.045 |
0.03 |
8.50-10.50 |
18.00-20.00 |
_ |
≥ 205 |
≥ 520 |
≥ 40 |
≤200 |
≤90 |
SUS304Ni9 |
0Cr18Ni9 |
304 |
1.4301 |
0.08 |
1 |
2 |
0.045 |
0.03 |
9.00-10.50 |
18.00-20.00 |
_ |
≥ 205 |
≥ 520 |
≥ 40 |
≤200 |
≤90 |
SUS316 |
0Cr17Ni12Mo2 |
316 |
1.4401 |
0.08 |
1 |
2 |
0.045 |
0.03 |
10.00-14.00 |
16.00-18.00 |
Mo 2.00-3.00 |
≥ 205 |
≥ 520 |
≥ 40 |
≤200 |
≤90 |
SUS316L |
00Cr17Ni14Mo2 |
316L |
1.4404 |
0.03 |
1 |
2 |
0.045 |
0.03 |
10.00-14.00 |
16.00-18.00 |
Mo 2.00-3.00 |
≥ 175 |
≥ 480 |
≥ 40 |
≤200 |
≤90 |
SUS321 |
0Cr18Ni10Ti |
321 |
1.4541 |
0.08 |
1 |
2 |
0.045 |
0.03 |
9.00-13.00 |
17.00-19.00 |
TI 5*C% |
≥ 205 |
≥ 520 |
≥ 40 |
≤200 |
≤90 |
SUS309S |
0Cr23Ni13 |
309S |
1.4833 |
0.08 |
1 |
2 |
0.045 |
0.03 |
12.00-15.00 |
22.00-24.00 |
_ |
≥ 205 |
≥ 520 |
≥ 40 |
≤200 |
≤90 |
SUS310S |
0Cr25Ni20 |
310S |
1.4845 |
0.08 |
1.5 |
2 |
0.045 |
0.03 |
19.00-22.00 |
24.00-26.00 |
_ |
≥ 205 |
≥ 520 |
≥ 40 |
≤200 |
≤90 |
Aciers inoxydables ferritiques |
SUH409L |
00Cr12Ti |
409L |
1.4512 |
0.03 |
1 |
1 |
0.04 |
0.03 |
_ |
10.50-11.75 |
TI 6*C%-0.75 |
≥ 175 |
≥ 360 |
≥ 25 |
≤175 |
≤80 |
SUS436L |
00Cr17Mo |
** |
** |
0.025 |
1 |
1 |
0.04 |
0.03 |
_ |
16.00-19.00 |
Mo 0.75-1.50 Ti NB ZR 8*C%+N%-0,80 |
≥ 245 |
≥ 410 |
≥ 20 |
≤230 |
≤96 |
SUS410 |
** |
410 |
1.4006 |
0.15 |
1 |
1 |
0.04 |
0.03 |
_ |
11.50-13.50 |
_ |
≥ 205 |
≥ 440 |
≥ 20 |
≤210 |
≤93 |
SUS410L |
00Cr12 |
** |
1.4003 |
0.03 |
1 |
1 |
0.04 |
0.03 |
_ |
11.00-13.50 |
_ |
≥ 195 |
≥ 360 |
≥ 22 |
≤200 |
≤88 |
SUS439 |
00Cr17 |
** |
1.451 |
0.03 |
1 |
1 |
0.04 |
0.03 |
0.5 |
17.00-19.00 |
TI 0.20+4 C+-1,10 al 0.15 N 0.030 |
≥ 205 |
≥ 415 |
≥ 22 |
≤200 |
≤89 |
SUS434 |
** |
434 |
1.4113 |
0.12 |
1 |
1 |
0.04 |
0.03 |
_ |
16.00-18.00 |
_ |
≥ 205 |
≥ 450 |
≥ 22 |
≤200 |
≤88 |
SUS444 |
00Cr18Mo2 |
444 |
1.4521 |
0.025 |
1 |
1 |
0.04 |
0.03 |
_ |
17.00-20.00 |
Mo 1.75-2.50 Ti NB ZR 8*C%+N%-0,80 |
≥ 245 |
≥ 410 |
≥ 20 |
≤230 |
≤96 |
SUS430 |
1Cr17 |
430 |
1.4016 |
0.12 |
1 |
1 |
0.04 |
0.03 |
_ |
16.00-18.00 |
_ |
≥ 205 |
≥ 420 |
≥ 22 |
≤200 |
≤88 |
Aciers inoxydables martensitiques |
SUS420J1 |
2Cr13 |
420 |
1.4021 |
0.16-0.25 |
1 |
1 |
0.04 |
0.03 |
_ |
12.00-14.00 |
_ |
≥ 225 |
≥ 520 |
≥ 18 |
≥ 234 |
≥ 97 |
SUS420J2 |
3Cr13 |
420JS |
1.4028 |
0.26-0.40 |
1 |
1 |
0.04 |
0.03 |
_ |
12.00-14.00 |
_ |
≥ 225 |
≥ 540 |
≥ 18 |
≥ 247 |
≥ 99 |