Spécification de la plaque en acier Corten | |
Standard Grade |
La norme ASTM : Corten A; Corten B; un588gr.A/B/gr gr..C/ Gr.K; A242; A606 type 4; A709 Gr 50W ; Fr10025 : S235J0W; S235J2W; S355J0W; S355J2W; S355K2W; S355J0WP; S355J2WP; S355J2G1W; S355J2G2W; S355K2G1W, S355K2G2W ; JIS G3114 : ; SMA SMA400AW400BW;; SMA SMA400CW490AW;; SMA SMA490BW490CW;; SMA SMA570W570P; JIS G3125 : SPA-H; SPA-C; GB/T 4171 : Q235NH; Q265BNB; Q310BNB; Q295NH; Q295BNB; Q355NH; Q355BNB; Q415NH; Q460NH; 1500NH; Q550NH; Le CT/T 1979 : 09CuPCrNi-A; 09CuCrNi-B; 05CuPCrNi; Q/BQB 340 : B460NQR; b490NQR; B480b600GNQR GNQR ;; |
Épaisseur | Tôles laminées à froid 0.5-2mm laminés à chaud (2-1002-300mm mm habituellement utilisé) |
Largeur | 1000-3000mm (1000-2200mm habituellement utilisé) |
Longueur | 1000-12000mm ou que votre demande |
Surface | Nettoyer, finition,le dynamitage et de la peinture selon l'exigence du client |
La livraison Membres |
Tôles laminées à chaud, contrôlée , la normalisation de laminage, recuit, la trempe, La trempe, N+T, q+T,et d'autres états de livraison sont disponibles comme requis |
Le certificat | API,ISO,SGS,BV,CE etc |
La qualité | MTC seront fournis avec des marchandises, troisième partie de l' inspection est acceptable, Par exemple BV,SGS. |
Paquet | En état de navigabilité d'exportation standard package,conviennent pour tous les types de transport, Ou comme nécessaire. |
Conteneur Taille |
20ft GP:5898mm(longueur)x2352mm(largeur)x2393mm(élevée) |
40ft GP:12032mm(longueur)x2352mm(largeur)x2393mm(élevée) | |
Durée du commerce | Ex-Work,FOB,CNF,CFR,CIF,etc |
L'application | Largement utilisé dans une variété de structures architecturales et techniques, telles que 1.) constructions métalliques tels que les bâtiments,ponts,les navires; 2.) tour de transmission, de la réaction tour ; 3.) La levée de la machinerie de transport; 4.) four;chaudières industrielles 5.) cadre du conteneur, l'entrepôt des marchandises d'étagères, etc. |
Plaque en acier Corten Composition chimique et les propriétés mécaniques |
||||||||
Grade | C | Si | Mn | P | S | Cr | Ni | Cu |
CORTEN UN | ≤0,12 | 0,25-0,75 | 0.20-0.50 | 0.07-0.15 | ≤0,030 | 0.50-1.25 | ≤0,65 | 0.25 -0.55 |
CORTEN B | ≤0,16 | 0.30-0.50 | 0.80-1.25 | 0,030 | ≤0,030 | 0,40-0.65 | 0.40 | 0.25 -0,40 |
Grade |
La force de rendement MPA | Résistance à la traction MPA | L'allongement % |
CORTEN UN | ≥355 | 470-630 | ≥20 |
CORTEN B | ≥345 | 470-630 | ≥20 |
Grade | C | Mn | Cr | Si | N | S | Cu | P | Ni | V | ||||||||||
Un588GrA | ≤0,19 | 0.80-1.25 | 0,40-0.65 | 0.30- 0,65 |
≤0,010 | 0,050 | 0,25-0.40 | 0,040 | ≤0,40 | 0. 01 -0. 10 |
||||||||||
Un588GrB | ≤0,20 | 0.75-1.35 | 0,40-0.70 | 0,15- 0.50 |
≤0,010 | 0,050 | 0.20-0.40 | 0,040 | ≤0,50 | 0. 01 -0. 10 |
||||||||||
Un588GrC | ≤0,15 | 0.80-1.35 | 0.30-0.50 | 0,15- 0.30 |
≤0,010 | 0,050 | 0.20-0.50 | 0,040 | 0,25-0,50 | 0.0 1- 0. 10 |
||||||||||
Matériel | Grade | La composition chimique, % | ||||||||||||||||||
C | Si | Mn | P | S | Cu | Cr | Ni | V | ||||||||||||
Q235NH | A-E | ≤ 0,13 | 0.10-0.40 | 0.20-0.60 | ≤ 0,13 | ≤ 0,13 | 0,25-0.55 | 0,40-0,80 | ≤ 0,65 | / | ||||||||||
Q295NH | A-E | ≤0,15 | 0.10-0.50 | 0.60-1.00 | ≤ 0,13 | ≤ 0,13 | 0,25-0.55 | 0,40-0,80 | ≤ 0,65 | / | ||||||||||
Q295BNB | A-E | ≤ 0,12 | 0.10-0.40 | 0.20-0.50 | ≤ 0,13 | ≤ 0,13 | 0,25-0.55 | 0,40-0,80 | 0.25 -0,50 |
/ | ||||||||||
Q355NH | A-E | ≤ 0,16 | ≤ 0,50 | 0.50-1.50 | ≤ 0,13 | ≤ 0,13 | 0,25-0.55 | 0,40-0,80 | ≤ 0,65 | / | ||||||||||
Q355BNB | A-E | ≤ 0,12 | 0.20-0,75 | ≤ 1,00 | ≤ 0,13 | ≤ 0,13 | 0,25-0.55 | 0,40-0,80 | ≤ 0,65 | / | ||||||||||
09CuPCrNi-A | / | ≤ 0,12 | 0.20-0,75 | 0.20-0.50 | 0.060-0.12 | ≤ 0,020 | 0,25-0,50 | 0.30-1.25 | 0.12 -0.65 |
/ | ||||||||||
09CuPCrNi-B | / | ≤ 0,12 | 0.10-0.40 | 0.20-0.50 | 0.060-0.12 | ≤ 0,020 | 0,25-0,50 | 0.30-0.65 | 0.25 -0,50 |
/ | ||||||||||
05CuPCrNi | / | ≤ 0,090 | 0,25-0,50 | 0.20-0.50 | 0.060-0.12 | ≤ 0,020 | 0,25-0,50 | 0.30-1.25 | 0.12 -0.65 |
/ | ||||||||||
B480GNQR | / | ≤ 0,12 | 0,25-0,75 | 0.20-0.50 | 0.070-0.15 | ≤ 0,030 | 0,25-0.55 | 0.30-1.25 | ≤ 0,65 | / | ||||||||||
Q450nqr1 | / | ≤ 0,12 | ≤ 0,75 | ≤ 1,50 | ≤ 0,025 | ≤ 0,020 | 0.20-0.55 | 0.30-1.25 | ≤ 0,65 | / | ||||||||||
SPA-H | / | 0.05-0.12 | 0,25-0,75 | 0.20-0.60 | 0.070-0.12 | ≤ 0,025 | 0,25-0,50 | 0.30-1.25 | ≤ 0,65 | / |
Grade | C | Mn | Cr | Si | Le CEV | S | Cu | P | |||
S355J2WP | ≤0,12 | ≤1,00 | 0.3-1.25 | ≤0,75 | ≤0,52 | ≤0,03 | 0,25-0.55 | 0.06 - 0,15 |
|||
Grade | La force de rendement MPA | Résistance à la traction MPA | L'impact | ||||||||
D'épaisseur mm | ≤16 | >16 ≤40 |
>40 ≤150 |
≤3 | >3 ≤100 | >100 ≤150 | Degré | J | |||
S355J2WP | ≥355 | ≥345 | - | 510-680 | 470-630 | - | -20 | 27 |
%C | %Tr | %Mn | %P | %S | %Cr | %Cu | %V | %Ni | Le rendement | En traction | L'élongation | |
Corten un | .12 | .25-.75 | .2-5. | .07-.15 | .03 | .5-1,25 | .25-.55 | .65 | 355 mpa | 470-630MPA | 20 % | |
Corten B | .16 | .3 .5 | .8-1,25 | .03 | .03 | .4-.65 | .25-.4 | .02-1. | 4. | 355 mpa | 470-630MPA | 20 % |
La norme ASTM A588 | .19 | .3-.65 | .8-1,25 | .05 | .04 | .4-.65 | .25-.4 | 4. | 340MPA | 480MPA | ||
La norme ASTM A242 type 1 | .12 | .75 | 1 | .06-.15 | .03 | .3-1,25 | .25-.55 | .52 | 4. | 355 mpa | 510-680 | L'impact-20/27J |
S355JOWP | .12 | .75 | 1 | .06-.15 | .035 | .3-1,25 | .25-.55 | N.009 | 4. | 355 mpa | 510-680 | L'impact0/27J |