La composition chimique
Acier commune de tuyaux en acier inoxydable/tube | |||||||||
Grade | La Composition chimique (%) | Mechanieal Performece | |||||||
C | Si | Mn | P | S | Ni | Cr | D'autres | La dureté | |
201 | ≤0,15 | ≤1,00 | 5.5/7.5 | ≤0,060 | ≤0,030 | 3.5/5.5 | 16.0/18.0 | - | HB≤241,DGRH≤100, HV≤240 |
202 | ≤0,15 | ≤1,00 | 7.5/10 | ≤0,060 | ≤0,030 | 4.0/6.0 | 17.0/19.0 | - | La DGRH≤195, HV≤218 |
304 | ≤0,08 | ≤1,00 | ≤2,00 | ≤0,045 | ≤0,03 | 8.0/11.0 | 18.00/20.00 | - | HB≤187,DGRH≤90,HV≤200 |
316 | ≤0,08 | ≤1,00 | ≤2,00 | ≤0,045 | ≤0,03 | 10.00/14.00 | 16.0/18.0 | Mo:2.00/3.00 | HB≤187, la DGRH≤90 HV≤200 |
316L | ≤0,03 | ≤1,00 | ≤2,00 | ≤0,045 | ≤0,03 | 10.00/14.00 | 16.0/18.0 | Mo:2.00/3.00 | HB≤187, la DGRH≤90 HV≤200 |
321 | ≤0,08 | ≤1,00 | ≤2,00 | ≤0,045 | ≤0,03 | 9.00/12.00 | 17.0/19.0 | Ti:5C-0.70 | La DGRH≤90, HV≤200 |
410 | ≤0,15 | ≤1,00 | ≤1,25 | ≤0,060 | ≤0,030 | ≤0,060 | 11.5/13.5 | - | HB≤183, la DGRH≤88 HV≤200 |
430 | ≤0,12 | ≤1,00 | ≤1,25 | ≤0,040 | ≤0,03 | - | 16.00/18.00 | - | HB≤183, la DGRH≤88 HV≤200 |
Différence de surface
No1 (laminés à chaud) : Après le laminage à chaud, le recuit, marinage et dephosphorization. La surface de la plaque d'acier traitée est une surface terne, un peu rugueux.Fournisseurs avec des licences commerciales vérifiées